| Grade | Density | T.R.S MPa | Hardness HRA | Performance & application recommended |
| YM6 | 14.9 | 2150 | 90.0 | Good wear resistance, used for hard wood, used for processing original wood, aluminum section bar, brass rod and cast iron. |
| YM6A | 14.9 | 1860 | 92.0 | Has wear resistance higher than YG6, used for processing hard wood, original wood, aluminum section bar, brass rod and cast iron. |
| YM8 | 14.7 | 2320 | 89.5 | Wear and percussion resistance , used for processing hard wood, soft wood, ferrous and non-ferrous. |
| YM2T | 14.5 | 2350 | 92.0 | Fine carbide, High wear resistance, high bending strength, high resistance to bonding, high thermal strength. Machining of refractory alloys, stainless steel and high manganese steel, etc. |
| YM25 | 14.5 | 2150 | 92.2 | Wear resistance and strength comparatively higher, suitable for processing cast iron, non-ferrous,metal and non-metallid materials. |
| Type | unit:mm | |||||||
| Type | L | W | T | Type | L | W | T | |
| 140 * W * T | 140 | 6 | 1.5-6.0 | 230 * W * T | 230 | 8 | 2.0-6.0 | |
| 140 * W * T | 140 | 8 | 1.5-.6.0 | 230 * W * T | 230 | 10 | 2.0-6.0 | |
| 140 * W * T | 140 | 10 | 1.5-6.0 | 230 * W * T | 230 | 12 | 2.0-6.0 | |
| 140 * W * T | 140 | 12 | 1.5-6.0 | 230 * W * T | 230 | 16 | 2.0-6.0 | |
| 140 * W * T | 140 | 14 | 1.5-6.0 | 230 * W * T | 230 | 18 | 2.0-6.0 | |
| 140 * W * T | 140 | 16 | 1.5-6.0 | 230 * W * T | 230 | 20 | 2.0-6.0 | |
| 140 * W * T | 140 | 18 | 1.5-6.0 | 230 * W * T | 230 | 22 | 2.0-6.0 | |
| 140 * W * T | 140 | 20 | 2.0-6.0 | 230 * W * T | 230 | 25 | 2.5-6.0 | |
| 140 * W * T | 140 | 22 | 2.0-6.0 | 230 * W * T | 230 | 28 | 2.5-6.0 | |
| 140 * W * T | 140 | 25 | 2.0-6.0 | 230 * W * T | 230 | 30 | 2.5-6.0 | |
| 165 * W * T | 165 | 6 | 1.5-6.0 | 230 * W * T | 230 | 32 | 2.5-6.0 | |
| 165 * W * T | 165 | 8 | 1.5-6.0 | 230 * W * T | 230 | 40 | 2.5-6.0 | |
| 165 * W * T | 165 | 10 | 1.5-6.0 | 320 * W * T | 320 | 8 | 2.0-6.0 | |
| 165 * W * T | 165 | 12 | 1.5-6.0 | 320 * W * T | 320 | 10 | 2.0-6.0 | |
| 165 * W * T | 165 | 14 | 1.5-6.0 | 320 * W * T | 320 | 12 | 2.0-6.0 | |
| 165 * W * T | 165 | 16 | 1.5-6.0 | 320 * W * T | 320 | 14 | 2.0-6.0 | |
| 165 * W * T | 165 | 18 | 1.5-6.0 | 320 * W * T | 320 | 16 | 2.0-6.0 | |
| 165 * W * T | 165 | 20 | 2.0-6.0 | 320 * W * T | 320 | 18 | 2.0-6.0 | |
| 165 * W * T | 165 | 22 | 2.0-6.0 | 320 * W * T | 320 | 20 | 2.0-6.0 | |
| 165 * W * T | 165 | 24 | 2.0-6.0 | 320 * W * T | 320 | 22 | 2.0-6.0 | |
| 165 * W * T | 165 | 25 | 2.0-6.0 | 320 * W * T | 320 | 24 | 2.0-6.0 | |
| 165 * W * T | 165 | 26 | 2.0-6.0 | 320 * W * T | 320 | 25 | 2.5-6.0 | |
| 165 * W * T | 165 | 28 | 2.0-6.0 | 320 * W * T | 320 | 28 | 2.5-6.0 | |
| 165 * W * T | 165 | 30 | 2.5-6.0 | 320 * W * T | 320 | 30 | 2.5-6.0 | |
| 165 * W * T | 165 | 32 | 2.5-6.0 | 320 * W * T | 320 | 32 | 2.5-6.0 | |
| 165 * W * T | 165 | 35 | 2.5-6.0 | 320 * W * T | 320 | 35 | 2.5-6.0 | |
| 165 * W * T | 165 | 40 | 2.5-6.0 | 320 * W * T | 320 | 40 | 2.5-6.0 | |
| ··· | ··· | ··· | ··· | ··· | ··· | ··· | ··· | |